Stienis cietlodes Ag5Cup 2.0mm*500mm (bez kat.)
Item No.
42100143-3
Typical Applications Ag5CuP HP is a silver-copper-phosphorous brazing alloy, with very good flow characteristics. It can be used to join copper to copper or copper based base materials (e.g. bronzes / brasses). Typical applications are in plumbing, in the electric and electromechanic industry,
Description
| Typical Applications |
| Ag5CuP HP is a silver-copper-phosphorous brazing alloy, with very good flow characteristics. It can be used to join copper to copper or copper based base materials (e.g. bronzes / brasses). Typical applications are in plumbing, in the electric and electromechanic industry, and in the refrigeration and airconditioning industry. |
 |
Properties |
| Typical brazing processes include flame, induction and furnace brazing. Ag5CuP should not be used on ferrous or nickel alloys, or alloys containing more than 10% of nickel, due to the formation of brittle intermetallic compounds which will cause failure of the joint. Good service performance are obtained on joints subject to vibrations. Corrosion resistance of Ag5CuP is generally satisfactory, except when the joint is contact with sulphurous atmospheres (especially at high temperatures); the alloy should therefore not be used to join parts that could come into contact with sulphur containing medias. |
| The phosphorus contained in the alloy acts as a fluxing agent, so that it is not necessary to use an additional flux when brazing copper to copper; however when joining copper based materials (e.g. bronzes / brasses) a proper flux should be used. Tensile strength of joints brazed with Ag5CuP will generally exceed base metals strength. Joint strength is however a function of various factors, such as: type of base metals to be joined, type of joint, joint clearance, brazing procedure, etc. |
| Physical & Technical properties | ||||||
| Melting Range (Solidus -liquidus), t°C | Minimum brazing temperature (flow point), t°C | Density, g/cm3 | Recomended joint gap, mm | Continuous service joint operating t°C | Max. short service joint operating t°C | |
643-771 | 710 | 8,2 | 0,05 - 0,2 | -55 / +150 | 200 | |
| Nominālais satāvs (īpatsvars, %) | ||||||
Ag | P | Cu | ||||
5 | 6,75 | bal. | ||||
| Standarti | ||||||
ISO 17672 | CuP 282 | |||||
EN 1044 | --- | |||||
AWS 5.8-04 | BCuP-7 | |||||