Elektrodi ELGA P48P 2.0mmx300mm/1,7kg

P 48M is a basic coated low hydrogen DC+ electrode designed for welding
mild and higher strength steels. It is particularly suitable for heavily restrained
sections and also steels with higher impurity levels. The electrode operates
with a very smooth and stable arc and shows no tendency to ''freeze'', even
on low current. Root passes can be welded with DC-. P 48M has very good fracture toughness at temperatures down to -50 °C.
Welding positions: PA, PB, PC, PE, PF.

Coating type:  Basic
Welding current: DC+/(-)
Hydrogen content / 100 g weld metal ≤ 4 ml
Metal recovery: 120%
Redrying temperature: 375-400 °C, 2h

Chemical composition, wt.%

	C	Si	Mn	P	S	Mo	Cu	V	Nb
Min		0,4	1,1
Typical	0,05	0,5	1,4	0,015	0,015
Max	0,09	1,75	1,6	0,020	0,020	0,1	0,2	0,05	0,05

Mechanical properties:

	Specified	Typical
Yield strength, Re:	420-500 MPa	480 MPa
Tensile Strength, Rm:	510-660 MPa	560 MPa
Elongation, A5	≥ 24%	28%
Impact energy, CV:	-50 °C • ≥47 J -46 °C • ≥27 J	-40 °C • 80 J -46 °C • 70 J -50 °C • 60 J

Classification:
EN ISO 2560-A E 42 5 B 42 H5
AWS A5.1 E 7018-1 H4R*