Stienis cietlodēšanas AG20 FC 2.0mm
Item No.
42100143-6
Range Of Applications Ag20FC is a general purpose, cadmium-free, silver brazing alloy, with high melting point and very wide melting range. It can be used to join ferrous, non ferrous and dissimilar metals and alloys, such as steel, copper, copper alloys. Due to its very wide melting range this
Description
Range Of Applications |
Ag20FC is a general purpose, cadmium-free, silver brazing alloy, with high melting point and very wide melting range. It can be used to join ferrous, non ferrous and dissimilar metals and alloys, such as steel, copper, copper alloys. Due to its very wide melting range this alloy is mostly used for brazing large and/or not uniform joints. Brazing procedures range from manual to induction techniques. When brazing in an oxidizing environment a proper flux should be used. Tensile strength of joints brazed with Ag20 will generally exceed base metals strength. Joint strength is however a function of various factors, such as: type of base metals to be joined, type of joint, joint clearance, brazing procedure, etc. |
Corresponding Standards | |
ISO 17672 | --- |
EN 1044 | AG206 |
AWS A5.8 | --- |
DIN 8513 | L-Ag20 |
Nominal composition (weight %) | ||||||
Type of Analysis | Ag | Cu | Zn | Si | ||
Weld Deposit | 20 | 44 | 36 | 0.15 |
Physical and technical properties | ||
Melting range (Solidus -Liquidus) | 690-810 C | |
Brazing temperature | ~820C | |
Density | 8,7 g/mm2 | |
Tensile strength (filler metal) | 43 kg/mm2 | |
Recommended joint gap | 0,075 - 0,2 mm | |
Continuous service joint temperature | -200/ +200C |
Characteristics Make-Up | ||||||
Product Code | Diameter x Length (mm) | Quantity per Box | Box Gross Weight (kg) | Boxes per Outer Box | Outer Box Gross Weight (kg) | Packaging Type |
0,5 /4.00 x 500/1000 | ||||||
Class of product |
Silver based brazing alloy, cadmium free. Product name Ag20 |
Specifications
Net Weight, kg | 0.1 |
Gross Weight, kg | 0.1 |
Gas volume, m 3 | 0 |
Standard rental price, EUR/day (exl. VAT) | 0 |